普通膠合板測試報告.

1、檢測報Test Report檢測工程:普通膠合板Test ItemsPlywood for General Use委托單位:獅山冠鋒木業(yè)制品Applicant Shishca Guanfeng Wood Products Co, Ltd.檢測類別：委托檢驗Test TypeEntrusted Test收樣日期：2018-10-22Received Date October 22nd,2018考前須知Precautions.檢測報告無本單位檢測專用章或騎縫章無效。Test report is invalid if not affixed with Authorized Stamp of Test

2、 or Paging Seal.檢測報告無審核人、批準人簽字無效。Test report is invalid without signature of verifier and approver.檢測報告涂改增刪無效。Test report is invalid only if being supplemented, deleted or altered.未經(jīng)本單位書面許可不得局部復制檢測報告(全部復制除外)。Without prior written permission of HJK, the test report cannot be reproduced, except in ful

3、l.除非另有說明，本報告檢測結果僅對測試樣品負責。Unless otherwise stated, the results shown in this test report are responsible for the delivered sample(s).對檢測報告假設有異議，應于收到報告之日起十五天內向檢測單位提出。Objections to the test report must be submitted to HJK within 15 days of report received date.樣品信息由送樣人提供，實驗室不負責核實信息真實性。The test applican

4、t is responsible for authenticity of sample information which not subject to verification of HJK LAB.上海宏駿科技實驗室具備由美國IAS認可的滿足ISO/IEC 17025要求的資質。Shanghai Hongjun Science & Technology Co., Ltd. is an ISO/IEC 17025-conforming test laboratory, which is accredited by International Accreditation Service, In

5、c.樣品描述/Sample Description收到的樣品為普通膠合板，樣品包裝完整、狀態(tài)完好。樣品規(guī)格尺寸如下表所示。The samples received are Plywood for general use. All test samples are packed well and kept in good conditions. The dimension specifications of the samples are shown in below table.測試工程尺寸規(guī)格 長*寬*厚(mm)數(shù)量(片)含水率Moisture Content100*25*8.53膠合強度B

6、onding strength100*25*8.512浸漬剝禺Impregnation Delamination75*75*8.56抗彎強度Bending Strength220*50*8.512彈性模量Bending Modulus of Elasticity220*50*8.512甲醛釋放量Formaldehyde Emission250*150*8.53.檢測標準/Testing Standards根據(jù)客戶要求，樣品根據(jù)如下標準進行測試：According to applicanfs requirements, the samples are tested according to th

7、e following standard:GB/T 9846-2015普通膠合板GB/T 17657-2013人造板及飾面人造板理化性能試驗ASTM D6007-2014 Standard Test Method for Determining Formaldehyde Concentrations in Air from Wood Products Using a Small-Scale Chamber.檢測描述/Testing Description測試環(huán)境溫度為232、相對濕度為605%。測試日期從2018年10月25日至11月6日 The temperature and relativ

8、e humidity of test environment are 232 and 60 + 5%, respectively. The tests were conducted from October 25th, 2018 through November 6th, 2018.檢測結果/Test Results序號No.測試工程Test Items單位Units標準要求Standard Requirements測試結果Test Results判定結果Conclusion1含水率Moisture Content%51411.7通過 Pass2膠合強度Bonding strengthMPan

9、類 20.701.83通過 Pass3浸漬剝離Impregnation Delaminationmm每個試件同一 膠層每邊剝離 長度累計不超 過 25mm。The cumulative peeling length of each specimen does not exceed that of 25mm in the same adhesive layer.15.0N/A4抗彎強度Bending StrengthMPa21224.2通過 Pass彈性模量 Bending Modulus of ElasticityMPa20002602通過 Pass5甲醛釋放量1Formaldehyde Em

10、issionppmW0.050.04通過 Pass備注/Notes:.浸漬剝離強度測試工程限值要求適用于相鄰單板紋理相互平行的樣品。The limit value requirements of impregnation delamination are applicable to applicable to test samples whose wood grain of adjacent veneers are perpendicular to each other.甲醛釋放量測試的指標要求參照加州空氣資源局93120法規(guī)表格一及美國聯(lián)邦法案40 CFR Part 770第 770.10中

11、要求的單板芯的硬木膠合板第二階段0.05ppm的限值要求。Index requirements for formaldehyde emission measurement are referenced to CARB 93120, Tablet, Phase 2& 770.10 of 40 CFR Part 770 limitation of0.05ppm forHWPW-VC.:初Reported by： *Reviewed by：附錄1 測試結果Appendix I - Test Data1.含水率/Moisture Content編號 No.長Length(mm)寬Width (mm)厚

12、Thickness (mm)氣干質量 Weight Before Conditioning( mm)絕干質量 Weight After Conditioning( mm)含水率 Moisture Content1100.2325.128.5813.0911.7211.7%2100.4525.318.4912.9711.6411.4%3100.3825.418.5413.4812.0412.0%2.膠合強度/Bonding strength編號 No.長度Length (mm)寬度 Width (mm)厚度Thickness (mm)極限載荷Ultimate Load(N)膠合強度Bonding

13、 strength (MPa)木破率wood failure percentage124.9025.538.991195.21.88100%224.4925.399.011465.82.36100%324.6025.468.961897.63.03100%424.1325.539.152485.44.03100%524.5025.479.011729.22.77100%623.9125.519.011662.02.72100%723.8525.419.031197.21.98100%824.4725.439.071650.82.65100%923.8725.599.081228.82.0110

14、0%1023.8025.429.142760.24.56100%1124.0825.579.012825.04.59100%1223.9425.559.053263.05.33100%3.浸漬剝離/Impregnation Delamination編號No.長度Length (mm)寬度Width (mm)厚度Thickness (mm)單邊剝離總長的最大值 Maximum Value ofSingle Delamination Bond Line (mm)175.3575.338.460.0275.2775.298.510.0375.2575.358.490.0475.3275.288.52

15、0.0575.1575.278.4915.0675.1775.298.480.04,抗彎性能/Bending Properties抗彎強度/Bending Strength編號No.寬Mid-Span Width (mm)厚Mid-Span Thickness (mm)極限載荷Ultimate Load (N)抗彎強度Bending Strength(MPa)150.168.59313.221.6250.068.49357.425.3350.178.55288.020.0450.128.55385.426.8550.168.57352.424.4650.178.52345.224.2750.0

16、48.54336.223.5849.998.55360.425.1950.168.55342.823.81050.098.61359.824.71150.138.57399.827.71250.168.59340.023.4彈性模量/Bending Modulus of Elasticity編號 No.寬 Mid-Span Width (mm)厚Mid-Span Thickness (mm)彈性段斜率Slope of Elastic Segment (N/mm)彈性模量Modulus of Elasticity (MPa)150.168.5955.662150250.068.4971.0728

17、49350.178.5563.522488450.128.5562.452448550.168.5762.472430650.178.5266.192620750.048.5471.542819849.998.5567.632658950.168.5567.2226331050.098.6170.5827121150.138.5770.5127451250.168.5969.142671附錄2樣品照片Appendix II - Sample Photosp ( fS 1I?fe豆5 (7SI o； 攣6I J06 08 7Z 09_OOPOS湍oQoe:加d6 Os06 018 OZO9 .產(chǎn) csBh|UK|llll|UH|lll!llll!lhUHir OK ol 03 oik,08 yL 09”O(jiān)GUOS仰?腦。件平坪品“J” M叫加加加加曲11岫曲!而inOS00k09,i 0憶0&乙0I C6,Qe 0jZ.0ft 即郵而n加加和而加喻加小而曲向ilw伽加Mu r